Carbon Steel Chemical Composition

MECHANICAL PROPERTIES									Mechanical Properties			Specific Requirement
MECHANICAL PROPERTIES									Tensile Strength	Yield Strength	Elngation	Specific Requirement
Spec.	WT	C%	Mn%	P% MAX	S% MAX	Si%	Cr%	Mo%	Mpa	Mpa	50mm MIN Longitudinal
ASTM A 53/A ASTM A 53/B ASTM A 106/A ASTM A 106/B ASTM A 106/C	AW AW AW AW AW	0.25MAX 0.30MAX 0.25MAX 0.30MAX 0.35MAX	0.95MAX 1.20MAX 0.27-0.93 0.29-1.06 0.29-1.06	0.050 0.050 0.025 0.025 0.025	0.060 0.060 0.025 0.025 0.025	- - 0.10MIN 0.10MIN 0.10MIN	- - 0.40MAX 0.40MAX 0.40MAX	- - 0.15MAX 0.15MAX 0.15MAX	331MIN 413MIN 330MIN 415MIN 485MIN	207 MIN 240MIN 205MIN 240MIN 275MIN	36 29.5 35/28 30/22 30/22	Cr Mo Cu Ni Va 0.40 0.15 0.40 0.40 0.08 five elements not to exceed 1%
ASTM A 179 ASTM A 214 ASTM A 192 ASTM A 209/T1 ASTM A 209/T1a ASTM A 209/T1B ASTM A 210/A-1 ASTM A 210/C	MW MW MW MW MW MW MW MW	0.06-018 0.18MAX 0.06-0.18 0.10-0.20 0.15-0.25 0.14MAX 0.27MAX 0.35MAX	0.27-0.63 0.27-0.63 0.27-0.63 0.30-0.80 0.30-0.80 0.30-0.80 0.93MAX 0.29-1.06	0.048 0.050 0.048 0.045 0.045 0.045 0.048 0.048	0.048 0.050 0.048 0.045 0.045 0.045 0.058 0.058	- - 0.25MAX 0.10-0.50 0.10-0.50 0.10-0.50 0.10MIN 0.10MIN	- - - - - - - -	- - - 0.44-0.65 0.44-0.65 0.44-0.65 - -	325MIN 385MIN 325MIN 380MIN 365MIN 415MIN 415MIN 485MIN	180MIN 180MIN 180MIN 205MIN 195MIN 220MIN 255MIN 275MIN	35.0 35.0 35.0 30/22 30/22 30/22 30/22 30/22	Hardness 72 HRB MAX Hardness 72 HRB MAX Hardness 77 HRB MAX Hardness 80 HRB MAX Hardness 81 HRB MAX Hardness 77 HRB MAX Hardness 79 HRB MAX Hardness 89 HRB MAX
ASTM A 213/T2 ASTM A 213/T5 ASTM A 213/T11 ASTM A 213/T12 ASTM A 213/T22	MW MW MW MW MW	0.10/0.20 0.15MAX 0.15MAX 0.15MAX 0.15MAX	0.30-0.61 0.30-0.60 0.30-0.60 0.30-0.61 0.30-0.60	0.045 0.030 0.030 0.045 0.030	0.045 0.030 0.030 0.045 0.030	0.10-0.30 0.50MAX 0.50-1.00 0.50MAX 0.50MAX	0.50-0.81 4.00-6.00 1.00-1.50 0.80-1.25 1.90-2.60	0.44-0.65 0.44-0.65 0.44-0.65 0.44-0.65 0.87-1.13	415MIN 415MIN 415MIN 415MIN 415MIN	205MIN 205MIN 205MIN 220MIN 205MIN	30/22 30/22 30/22 30/22 30/22	Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX
ASTM A 333/1 ASTM A 333/6 ASTM A 334/1 ASTM A 334/6	AW AW AW AW	0.30MAX 0.30MAX 0.30MAX 0.30MAX	0.40-1.06 0.29-1.06 0.40-1.06 0.29-1.06	0.025 0.025 0.025 0.025	0.025 0.025 0.025 0.025	- 0.10MIN - 0.10MIN	- - - -	- - - -	380MIN 415MIN 380MIN 415MIN	205MIN 240MIN 205MIN 240MIN	25/20 30/22 35/28 30/22	Impact AS-50F FOR 40X10J/18/14 -50F 40X10J/18/14 90 HRB MAX
ASTM A 335/P1 ASTM A 335/P2 ASTM A 335/P5 ASTM A 335/P9 ASTM A 335/P11 ASTM A 335/P12 ASTM A 335/P22	AW AW AW AW AW AW AW	0.10-0.20 0.10-0.20 0.15MAX 0.15MAX 0.15MAX 0.15MAX 0.15MAX	0.30-0.80 0.30-0.61 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.61 0.30-0.60	0.025 0.025 0.025 0.025 0.025 0.025 0.025	0.025 0.025 0.025 0.025 0.025 0.025 0.025	0.10-0.50 0.10-0.30 0.50MAX 0.25-1.00 0.50-1.00 0.50MAX 0.50MAX	- 0.50-0.81 4.00-6.00 8.00-10.00 1.00-1.50 0.80-1.25 1.90-2.60	0.44-0.65 0.44-0.65 0.45-0.65 0.09-1.10 0.44-0.65 0.44-0.65 0.87-1.13	380MIN 380MIN 415MIN 415MIN 415MIN 415MIN 415MIN	205MIN 205MIN 205MIN 172MIN 205MIN 205MIN 205MIN	30/22 30/22 30/22 30/22 30/22 50/22 30/22
BS/3059/1/33 BS/3059/2/33 BS/3059/2/45 BS/3059/2/620		0.15MAX 0.15MAX 0.12-0.18 0.10-0.15	0.30-0.70 0.40-0.70 0.90-1.20 0.40-0.70	0.050 0.050 0.035 0.040	0.050 0.050 0.035 0.040	- 0.10-0.35 0.10-0.35 0.10-0.35	- - - 0.70-1.10	- - - 0.45-0.65	324-441 324-441 441-560 441-618	186MIN 186MIN 245MIN 235MIN	25 21 22 22
DIN/17175/ST35.8 DIN/17175/ST45.8 DIN/17175/15MO3 DIN/17175/13CrMO44 DIN/17175/10CrM910		0.17MAX 0.22MAX 0.12-0.20 0.10-0.18 0.15MAX	0.40MIN 0.45MIN 0.50-0.80 0.40-0.70 0.40-0.60	0.040 0.040 0.040 0.040 0.040	0.040 0.040 0.040 0.040 0.040	0.35MAX 0.10-0.35 0.10-0.35 0.10-0.35 0.15-0.50	- - - 0.70-1.60 2.0-2.5	- - 0.25-0.35 0.40-0.50 0.9-1.10	340-441 441-540 441-540 441-570 441-570	235MIN 255MIN 284MIN 294MIN 294MIN	25 25 21 22 22
ASTM A 199/T5 ASTM A 199/T11 ASTM A 199/T22 ASTM A 199/T4 ASTM A 199/T7 ASTM A 200/T5 ASTM A 200/T11 ASTM A 200/T22 ASTM A 200/T4 ASTM A 200/T7 ASTM A 199/T9	MW MW MW MW MW MW MW MW MW MW MW	0.50-0.15 0.50-0.15 0.50-0.15 0.15MAX 0.15MAX 0.15MAX 0.50-0.15 0.50-0.15 0.50-0.15 0.15MAX 0.15MAX	0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60	0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030	0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030	0.50MAX 0.50-1.00 0.50MAX 0.50-1.00 0.50-1.00 0.50-1.00 0.50-1.00 0.50MAX 0.50-1.00 0.50-1.00 0.25-1.00	4.00-6.00 1.00-1.50 1.90-2.60 2.15-2.85 6.00-8.00 4.00-6.00 1.00-1.50 1.90-2.60 2.15-2.85 6.00-8.00 8.00-10.0	0.45-0.65 0.44-0.65 0.87-1.13 0.44-0.65 0.45-0.65 0.45-0.65 0.44-0.65 0.87-1.13 0.44-0.65 0.45-0.65 0.90-1.10	415MIN 415MIN 415MIN 415MIN 415MIN 415MIN 415MIN 415MIN 415MIN 415MIN 415MIN	170MIN 170MIN 170MIN 170MIN 170MIN 170MIN 170MIN 170MIN 170MIN 170MIN 170MIN	30/22 30/22 30/22 30/22 30/22 30/22 30/22 30/22 30/22 30/22 30/22	Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX Hardness 85 HRB MAX